Journal of Siberian Federal University. Engineering & Technologies. 2015 8 (5)

Authors

Dyja, Henryk; Ozhmegov, Kirill V.; Kawałek, Anna; Galkin, Aleksander M.

Contact information

Dyja, Henryk:Czestochowa University of Technology (CUT) 19 Al. Armii Krajowej, Częstochowa, 42-200, Poland; E-mail: ; Ozhmegov, Kirill V.:National University of Science and Technology “MISIS” (MISIS) 4 Leninskiy, Moscow, 119049, Russia; Kawałek, Anna:Czestochowa University of Technology (CUT) 19 Al. Armii Krajowej, Częstochowa, 42-200, Poland; Galkin, Aleksander M.:National University of Science and Technology “MISIS” (MISIS) 4 Leninskiy, Moscow, 119049, Russia

Keywords

rheological properties; zirconium alloys; process modeling; metal forming

Abstract

В настоящей работе поставлена задача исследования реологических свойств модифицированных по химическому составу сплавов циркония систем Zr – Nb и Zr – Nb – Sn применительно к условиям различных процессов обработки металлов давлением (ОМД) при производстве труб и прутков. Для этого были выполнены комплексные пластометрические исследования новых марок сплавов с целью получения экспериментальных данных по величине сопротивления деформации σs и предельной пластичности Λр этих материалов. Испытания проводились на современной пластометрической установке в широком диапазоне термомеханических условий деформирования по различным законам нагружения. На основе экспериментальных данных о механических свойствах исследуемых материалов осуществлена разработка режимов технологических процессов ОМД с использованием программного комплекса для компьютерного моделирования Forge 2008

In this work, a task was set to study the rheological properties of zircon-based alloys with a modified chemical composition of the Zr – Nb and Zr – Nb – Sn systems with respect to the conditions of different processes of pressure metal treatment during manufacturing of pipes and rods. For this purpose, complex plastometric tests of new grades of alloys were carried out to obtain experimental data on the deformation resistance value σp and maximum permissible plasticity Λр of these materials. The tests were carried out on a modern plastometric apparatus in a wide range of thermal mechanical conditions of deformation according to different forms of loading. On the basis of the experimental data on the mechanical properties of the materials under study, pressure metal treatment processes were developed using the Forge 2008 computer modeling software package