Siberian Federal University 
- Issue
- Journal of Siberian Federal University. Engineering & Technologies. 2012 5 (1)
- Authors
- Shimanskiy, Igor A.; Babkin, Vladimir G.; Frizorger, Vladimir K.; Goloskin, Evgeniy S.; Nabiulin, Alexey B.
- Contact information
- Shimanskiy, Igor A. : Siberian Federal University , 79 Svobodny, Krasnoyarsk, 660041 Russia , e-mail: ; Babkin, Vladimir G. : Siberian Federal University , 79 Svobodny, Krasnoyarsk, 660041 Russia; Frizorger, Vladimir K. : «Rus-engineering» Ltd , Krasnoyarsk, 660049 Russia; Goloskin, Evgeniy S. : Siberian Federal University , 79 Svobodny, Krasnoyarsk, 660041 Russia; Nabiulin, Alexey B. : Siberian Federal University , 79 Svobodny, Krasnoyarsk, 660041 Russia
- Keywords
- cast iron; gas manifold; skirts; high temperature gas corrosion; protective coatings; mechanical activation
- Abstract
The influence of initial components mixture mechanical activation on the synthesis processes in enamel mass and on the molten enamel adhesion to the metal was investigated. Its established, that the process of albite formation in the coating material intensifies by components mixture activation. On the base of measured contact angles of cast iron with molten enamel was revealed, that adhesion of the molten enamel to the metal noticeably increases by initial components activation.
- Pages
- 63-71
- Paper at repository of SibFU
- https://elib.sfu-kras.ru/handle/2311/2876